OPVDS with this nanodiamond size exhibited highest power conversion efficiency in a previous study [10].
The performance of OPVDs with active film doped with nanodiamond at various concentrations is shown in Table 1.
Hybrid OPVDs with P3HT:PCBM/nanodiamond films with nanodiamond levels of 0, 0.5, 1.5, and 3 wt% have power conversion efficiency values of 1.82%, 1.96%, 2.25%, and 1.38%, respectively.
Figure 6 shows the EQE spectra for hybrid OPVDs with various nanodiamond concentrations measured at room temperature.
The results reveal that 1.5 wt% nanodiamond doping into OPVDs increases the short-circuit current density from 6.1 to 7.28 mA x [cm.sup.-2] at e-spray method, which is due to e-spray increase interface with PEDOT:PSS and active layer.