A comparison of the weight reduction of TPE1, TPE2, TPE3, and TPE4 towards thermal degradation was done by using TGA at a heating rate of 10[degrees]C [min.sup.-1], wherein the samples were being heated starting from room temperature to 500[degrees]C (Figure 3).
Therefore, it shows that TPE3 and TPE4 have a higher thermal resistance compared to TPE1 and TPE2.
It was revealed that three steps were involved in the thermal degradation of the TPE1 and two steps were showed for the TPE2, TPE3, and TPE4.
The DTG thermogram of TPE1 had revealed a peak at a maximum temperature of 188.99[degrees]C in which it represents the evaporation of glycerol.